LEADA N1 Paste compound
LEADA N1 Polishing Paste is our only paste compound in the LEADA 3-stage paint correction system. Its cutting performance, handling and final polishing result are highly comparable to Farecla G3. Designed as Step 1 heavy cut compound for paint correction.
Formulated with stable abrasive particles, LEADA N1 paste compound efficiently removes P1200–P1500 grit sanding marks, heavy oxidation, orange peel, paint runs and overspray on automotive clear coat. It works both by hand and machine (rotary & DA polisher), matching the classic work habit of Farecla G3.
This thick paste compound delivers consistent cutting power with low splatter. It is silicone-free, safe for bodyshop refinish and ceramic coating prep. After finishing Step1 with LEADA N1, proceed to Step2 Medium Cut Polish and Step3 Smooth Finishing Polish to achieve perfect mirror finish.
Application: Step 1 – Heavy Cut Polishing
Thoroughly clean, degrease and dry the cool paint surface. Ensure the surface is free of dirt, dust and wax.
LEADA N1 is our only paste compound. Use coarse wool pad; apply an appropriate amount of paste onto the pad.
Operate polisher at 1200–1800 RPM, work on small sections (40×40cm) at a time. Hand polishing is also available for local defect treatment.
Spread the paste thinly first, then apply firm pressure to remove deep defects: P1200–P1500 grit sanding marks, orange peel, heavy oxidation, paint runs and overspray.
Once defects are removed and cutting is completed, reduce pressure slightly. Wipe residues off with a clean microfiber towel.
After Step1 correction, move to Step2 LEADA Medium Cut Polish to refine the paint surface.
Note: Do NOT apply under direct sunlight or on hot paint panels.